PRODUCT CODE : 107634
GLOSS PAPER SELF ADHESIVE LABEL WITH ALIMINIUM BARRIER AND TYRE ADHESIVE

Product
Paper-based face with aluminium barrier to prevent plasticizer migration and improve adhesion to the tyre surface.

Use
Specially designed for labelling tyres and other rough surfaces

Typical Technical Values
Substance                   : 82 gr/m2       ISO 536
Caliper                        : 59 µm           ISO 534
Tensile Strength         : 5.2 Kn/m       ISO 1924/1
Brightness                  : % 76              ISO 2470/1
Gloss                           : % 55              Hunter 75°
Printability                  :Flexo, letterpress and thermal transfer.

Adhesive
Type                            : Extra-strong permanent hotmelt adhesive           
Composition               : Rubber hotmelt
Use                             : Designed specifically for heavy duty applications involving rough surfaces

PRODUCT CODE : 205172
PET125 WHITE SELF ADHESIVE LABEL FILM

A white gloss heat stabilised polyester film. The smooth surface is covered with a topcoat for very good ink anchorage.
Basis Weight 185 g/m² ISO 536
Caliper 125 µm ISO 534
Adhesive
Solvent rubber based adhesive used in the tyre vulcanization process.
Liner
A clear polyester liner . The polyester liner giving optimum smoothness to the adhesive layer.
Basis Weight 70 g/m² ISO 536
Caliper 50 µm ISO 534
Transparency 99 % DIN 53147
Laminate
Total Caliper 200 µm±10% ISO 534
Performance data
Service temperature -40°C to 80°C
Maximum Peak Temperature-1hr 200 °C
Peel Adhesion 90° 8 N/25mm FTM2 HDPE 24hr
Initial Tack (HDPE) 15 N/25mm FTM9 HDPE
Minimum Vulcanization Temperature 160 °C
Maximum Vulcanization Temperature 220 °C

PRODUCT CODE : 206061
TRANSFER PET36 WHITE FILM SELF ADHESIVE LABEL

A gloss white polyester film. The smooth surface is covered with a topcoat for excellent ink anchorage.

Basis weight: 54g/m² ISO 536
Calliper: 36 µm ISO 534

Adhesive
Permanent high coat weight silicone adhesive. Good final adhesion on textured and low surface energy substrates. It features superior resistance against temperature extremes, moisture, chemicals and UV light.

Liner
PET75: A clear polyester liner, giving optimum smoothness to the adhesive layer.

Performance data
Adhesive Type: Silicone adhesive, solvent based
Coat weight: 50 g/sqm
Initial Tack: 25 N / 25 mm FTM 9 glass
Peel Adhesion: 16 N / 25 mm FTM 1 steel 24 hrs.
Min. application temperature: +5 °C
Min. service temperature: -80 °C
Max. service temperature: +150 °C

PRODUCT CODE : 206051
TRANSFER PET WHITE FILM SELF ADHESIVE LABEL

A white polyester material featuring excellent chemical resistance of the thermal transfer print.Combined with the high coat weight rubber hybridised acrylic adhesive featuring excellent chemical and heat resistance.

Facestock
A gloss white polyester film. The smooth surface is covered with a topcoat for very good ink anchorage.
Basis Weight 76 g/m² ASTM D 4321
Caliper 50 µm ASTM D 4321

Adhesive
Rubber hybridised acrylic (RHA) adhesive. It combines extreme high final adhesion on a wide variety of surfaces including textured and low surface energy substrates with excellent chemical and temperature resistance.
The high adhesive coat weight of 45 g/m² makes this adhesive ideal for labelling rough plastics and other rough surfaces.

Liner
Both sides siliconized glassine white paper, wood- free, super calandered and extremely tough and tear-restistent despite its thinness.

PRODUCT CODE : 206227
TRANSFER PET WHITE FILM SELF ADHESIVE LABEL

Basis weight: 55g/m²  ISO 536
Calliper: 50 µm  ISO 534

Adhesive
Heat stabilized, permanent acrylic adhesive. High resistance against temperature peaks and moisture.

Liner
Super-calendered siliconized glassine paper. Without back imprint.

Basis weight: 78g/m²
Caliper: 68 µm

Performance data

Coat weight 40 g/sqm
Initial tack 800 N/m FTM 9 glass
Peel Adhesion: 680 N/m FTM 2 steel 24 hrs.
Min. application temperature: +5 °C
Min. service temperature: -40 °C
Max. peak temperature: +220 °C

PRODUCT CODE : 207352
TRANSFER HDPE 95 MATT FILM SELF ADHESIVE LABEL

A matt white HDPE film, coated with a topcoat which offers excellent printability.

Basis weight: 75 g/m² ISO 536
Calliper: 95 µm ISO 534

Adhesive
High tack, rubber based hotmelt adhesive. high initial tack and peel adhesion, also on rough and slightly contaminated substrates, for example rough building materials and timber.

Liner
White super-calendered siliconized glassine paper. Without back imprint.

Basis weight: 70 g/m² ISO 536
Caliper: 63 µm ISO 534

Laminate
Total Caliper: 204 µm ± 10% ISO 534

Performance data
Initial Tack: 35 N/25mm FTM 9 glass
Peel Adhesion: 21 N/25mm FTM 2 steel 24 hrs.
Min. application temperature: 0 °C
Service temperature: -40 °C to 70°

PRODUCT CODE : 207029
WHITE POLYETHYLENE PE100 FILM SELF ADHESIVE LABEL

A white polyethylene film with a print-receptive topcoat.
Basis Weight 92 g/m² ISO 536
Caliper 93 µm ISO 534

Adhesive
New generation of an emulsion acrylic adhesive for labelling oil cans.
Liner
White, a supercalendered glassine paper.The liner is made from FSC® certified paper

Basis Weight 59 g/m² ISO 536
Caliper 53 µm ISO 534

Laminate
Total Caliper 166 µm±10% ISO 534

Performance Data
Initial Tack 16 N/25mm FTM 9 Glass Peel Adhesion 90°
10 N/25mm FTM 2 St.St.
Min. Application Temp. 0 °C
Service Temperature -20 °C to 80 °C

PRODUCT CODE : 210125
POLYIMIDE II WHITE FILM SELF ADHESIVE LABEL

A durable polyimide film with a high-temperature resistance high opacity, semi-matt white topcoat

Adhesive
High-temperature resistance, permanent, acrylic adhesive. The high temperature resistant acrylic adhesive is designed for labelling printed circuit boards. It withstands high temperatures and corrosive solvents.

Liner
White, siliconized, bleached, super-calendered liner. Good die-cutting and matrix stripping. Suitable for roll-to-roll conversion.

Basis weight: 80 g/m² ISO 536
Caliper: 70 µm ISO 534

Laminate
Total caliper: 168 µm